Quasi-solid-state sodium-ion hybrid capacitors enabled by UiO-66@PVDF-HFP multifunctional separators: Selective charge transfer and high fire safety

The practical application of sodium-ion hybrid capacitors is limited by their low energy densities resulted from the kinetics mismatch between cathodes and anodes, and the fire safety related to the flammable electrolyte-separator system. Hence, we report a rational design of metal–organic frameworks (MOFs, UiO-66) modified PVDF-HFP separator. High tensile strength and dimensional thermal stability of the separator reduce the risk of electrode short circuit caused by the separator deformation. MCC test demonstrates a reduction of 75% in peak heat release rate (pHRR), indicating an enhanced fire-resistant property of the separator. This is due to the transformation of UiO-66 into ZrO 2 accompanied by the consumption of oxygen and the formation of the barrier char that suppresses further heat release. Quasi-solid-state electrolyte prepared based on this separator presents an enhanced ionic conductivity of 2.44 mS cm −1 and Na-ion transference number of 0.55, which are related to the high porosity (>70%) and electrolyte uptake (~320%) of the separator. Moreover, the open metal sites of UiO-66 can capture PF 6 – and consequently liberate the Na + for faster migration, thus reducing the kinetics mismatch between cathodes and anodes. Such multifunctional separator enables the quasi-solid-state Na-ion hybrid capacitor to achieve high energy density (182 Wh kg −1 @31 W kg −1 ) and power density (5280 W kg −1 @22 Wh kg −1 ), as well as excellent cyclic stability (10,000 cycles @1000 mA g −1 ).