Effect of modified bamboo lignin replacing part of C5 petroleum resin on properties of polyurethane/polysiloxane pressure-sensitive adhesive and its application on the wood substrate

This paper reports a fresh and robust strategy to develop polyurethane/polysiloxane pressure-sensitive adhesives (PSAs) with excellent properties by replacing part of C5 petroleum resin with modified lignin. A unique aspect of this work is the use of renewable lignin to obtain modified monomers . The phenolic hydroxyl group of lignin is increased by 21.4% after demethylation , which will help to introduce 6-bromo-1-hexene into the lignin structure through Williamson method. The L 3 lignin and C5 petroleum resin are mixed with polyurethane/polysiloxane prepolymer , and furthermore a series of PSAs are obtained under ultraviolet light. It turns out that L 3 lignin can not only replace part of C5 petroleum resin, but also obtain attractive and controllable features. Especially when the mass ratio of C5 petroleum resin to L 3 lignin is 6:4, compared with pure C5 petroleum resin, the 180° peel strength and the shear strength of PU46 are increased by 24.1% and 91.5% respectively. Additionally, the shear strength on the wood substrate is increased by 320.6%. This study provides an effective method for the preparation of high value-added lignin PSA, and expands the application fields of PSA.