Sieve-Like CNT Film Coupled with TiO2 Nanowire for High-Performance Continuous-Flow Photodegradation of Rhodamine B under Visible Light Irradiation

Continuous-flow photoreactors hold great promise for the highly efficient photodegradation of pollutants due to their continuity and sustainability. However, how to enable a continuous-flow photoreactor with the combined features of high photodegradation efficiency and durability as well as broad-wavelength light absorption and large-scale processing remains a significant challenge. Herein, we demonstrate a facile and effective strategy to construct a sieve-like carbon nanotube (CNT)/TiO2nanowire film (SCTF) with superior flexibility (180° bending), high tensile strength (75–82 MPa), good surface wettability, essential light penetration and convenient visible light absorption. Significantly, the unique architecture, featuring abundant, well-ordered and uniform mesopores with ca. 70 µm in diameter, as well as a homogenous distribution of TiO2nanowires with an average diameter of ca. 500 nm, could act as a “waterway” for efficient solution infiltration through the SCTF, thereby, enabling the photocatalytic degradation of polluted water in a continuous-flow mode. The optimized SCTF-2.5 displayed favorable photocatalytic behavior with 96% degradation of rhodamine B (RhB) within 80 min and a rate constant of 0.0394 min−1. The continuous-flow photodegradation device made using SCTF-2.5 featured exceptional photocatalytic behavior for the continuous degradation of RhB under simulated solar irradiation with a high degradation ratio (99.6%) and long-term stability (99.2% retention after working continuously for 72 h). This work sheds light on new strategies for designing and fabricating high-performance continuous-flow photoreactors toward future uses.Keywords:sieve-like CNT film;TiO2nanowire;continuous-flow device;photodegradation;pollutant