Influence of dextrin content and sintering temperature on the properties of coal fly ash-based tubular ceramic membrane for flue gas moisture recovery

In this paper, in order to reduce the preparation cost of high-performance ceramic membrane , coal fly ash-based tubular ceramic membrane for flue gas moisture recovery was prepared, and its properties were optimized from two aspects: pore-forming agent (dextrin) content and sintering temperature . The results show that the ceramic membrane with dextrin content of 3 wt.% and sintering temperature of 1150 ℃ has the best performance. Through characterization, the ceramic membrane exhibits an open porosity of 42.0 %, mechanical strength of 26.6 MPa, average pore size of 0.49 μm, pure water flux of 5616 L/(m 2 barh). And, it has excellent corrosion resistance in acid and alkali. In addition, the flue gas moisture recovery performance of coal fly ash-based tubular ceramic membrane was studied experimentally. The highest water recovery ratio and the highest recovered water flux is 87.7 % and 6.01 kg/(m 2 h, respectively.