Electrical properties and temperature stability of SrTiO3-modified (Bi1/2Na1/2)TiO3-BaTiO3-(K1/2Na1/2)NbO3 piezoceramics

SrTiO 3 -modified lead-free piezoelectric ceramics, (0.93- x )Bi 0.5 Na 0.5 TiO 3 - x SrTiO 3 -0.06BaTiO 3 -0.01 K 0.5 Na 0.5 NbO 3 [(BNT- x ST)-BT-KNN, x = 0-0.06], were prepared using a conventional solid-state reaction method. The XRD structure analysis and electric properties characteristics revealed the ST-induced phase transformation from the ferroelectric phase to the relaxor phase and their coexistence state. Benefiting from the ST-destructed ferroelectric long-range orders, the high normalized strain value of 600 pm/V was obtained in the (BNT-0.02ST)-BT-KNN ceramic at 5 kV/mm. The ST-generated relaxor phase was found to have a constructive effect on improving the temperature stability and restraining the hysteresis of the electric-field-induced strain. The normalized strain of (BNT-0.06ST)-BT-KNN ceramics could be kept at a high value ~337 pm/V at elevated temperature up to 120°C.