Synergy coordination of cellulose-based dialdehyde and carboxyl with Fe3+ recoverable conductive self-healing hydrogel for sensor

A novel dual ionic network cellulose-based composite conductive self-healing hydrogel was fabricated with high elongation, rapid recoverability, high conductive sensitivity, self-healing ability and good biocompatibility. The hydrogel was constructed by the synergistic complexations of new-fashioned bidentate aldehyde groups on dialdehyde cellulose nanofibers (DACNFs) and carboxyl groups of acrylic acid (AA) with Fe 3+ . The elongation (~1300%) of the hydrogel containing 1 wt% DACNFs was approximate 13-fold of the pure PAA hydrogel and can recover to original state within 2 min after 80% compression. The self-healing efficiency increased with the addition of DACNFs in the dual ionic network cellulose-based composite conductive self-healing hydrogel. The hydrogel configured for a wearable test and showed high stretching sensitivity with a gauge factor of 13.82 at strain within 1.6%. The gauge factor (GF) decrease with the incremental strain within 20%. GF were 0.696 between 20% and 300% strain, 0.837 within 300% and 500%. Meanwhile, the current had a good linear relationship with the bending angles of hydrogels and pressure on hydrogels, which may provide a great potential in monitor both minor variations and large movements.