Design of recyclable, fast-responsive and high temperature shape memory semi-aromatic polyamide

Development of high temperature shape memory polymers with fast response time and recyclable performance is highly desired. In this study, a new semi-aromatic tri-amine (TRIA) containing thioether unit is prepared through the reaction of trifluoro-monomer and p-mercaptoaniline (p-MA). It is conducted to polymerize with 4,4′-thiodibenzoyl chloride (TDC) and different ratios of diamine (both of them contained flexible thioether group) to supply a series of slightly crosslinking semi-aromatic polyamide . It is found that the resultant polymers had excellent thermal properties (T g , 237.9–245.8 °C, T d , 430.9–436.5 °C) and mechanical properties (tensile strength, 74–100 MPa). Because of the introduction of the large amount of flexible thioether group, the resultant polyamides can be dissolved in some aprotic solvents , and can be processed with solution method to fabricate a series of fast-responsive shape memory film (SMF) with a responsive time of 6–8 s, recovery rate of 98–99.5% after 20 cycles. What's more, the oxidized film can even lift a weight equal to about 2–3 times (vertical direction) and 5–8 times (horizontal direction) of its own weight. Interestingly, unlike other shape memory polymers, these SMF after multiple processes (after bending-recovery cycle at high temperature) can still be processed repeatedly with a solution route, which supplies a novel and recyclable candidate for excellent performance SMP. It is expected to be used in solar cell wingspan actuator to light the satellite weight.