Preparation and properties of high-porosity ZrB2-SiC ceramics by water-based freeze casting

The development of novel cermet composites based on porous ceramics with high porosity, interconnected pore structure and good mechanical property has attracted considerable attention in engineering application. In this work, water-based freeze casting process was employed to fabricate ZrB 2 -SiC porous ceramic with aligned lamellar-channels structure using PAA-NH 4 as the dispersant. The results revealed that the well-dispersed suspension with best rheological behavior was obtained using 1.0 wt% PAA-NH 4 at pH 9. The crack-free porous ceramic exhibited small volume shrinkage ranging from 2.59 % to 1.87 %. By varying the solid loading, the fabricated samples displayed a tailored porosity ranging from 76.12% to 59.37% and an excellent compressive strength of 7 MPa to 78 MPa. After oxidation, the samples displayed a decreased porosity and an increased compressive strength. The ZrB 2 ­SiC porous ceramic fabricated in this work will be a promising candidate for the framework of cermet composite.