Effect of Eu3+ doping on luminescence properties of a KAlSiO4:Sm3+ phosphor

This study presents the photoluminescence characteristic analysis of a series of red phosphors of KAlSiO 4 :1.5 mol%Sm 3+ , x mol%Eu 3+ ( x  = 2, 3, 4, 5, 6, 7) prepared via high-temperature solid-phase reaction. The results show that the X-ray diffraction (XRD) refinement results are reliable. The unit cell parameters and volume gradually decrease as the Eu 3+ concentration increases, resulting in a grain size reduction of 10.22%. When x  = 6, the emission peaks of Sm 3+ at 564, 601, and 651 nm disappear completely, and the corresponding full width at half maximum becomes 0. At 610 nm, the emission peak intensity of Eu 3+ is increased by a factor of 4.8. The resonant non-radiative energy transfer effect is greater than the co-excitation effect. A maximum energy transfer efficiency of 97.8% is achieved. The integral area at 610 nm is as high as 85%. The color purity of the phosphor is as high as 92.97%, and the internal quantum yield gradually changes from 32% to 51%. Ultimately, these results confirm that the silicate phosphor is suitable for the red component in the three primary color phosphors of white light-emitting diodes.