ZIF-derived mesoporous carbon materials prepared by activation via Na2SiO3 for supercapacitor

Metal organic frameworks (MOFs) derived carbonaceous materials have a wide range of applications in the fields of energy storage, catalysis, adsorption and separation, etc . Especially, zeolitic imidazolate framework-8 (ZIF-8) is an excellent candidate to synthesize porous carbon due to the large surface area and high nitrogen content. However, the dominated microporous structure of ZIF-8-derived carbon significantly hinders ionic mass transfer, limiting the improvement of performance. Herein, MOF-derived mesoporous carbon was prepared using ZIF-8 as carbon precursor and cheap sodium silicate (Na 2 SiO 3 ) as activator. The introduction of Na 2 SiO 3 created rich mesoporous structure and increased specific surface area, as well as the effects of pyrolysis temperature and Na 2 SiO 3 dosage on performance was also investigated. The obtained ZIF-derived porous carbon exhibits good electrochemical performance with specific capacitance of 263 F/g at 1 A/g and excellent cycle life (96.07% after 10,000 GCD cycles) in supercapacitor. The use of cheap Na 2 SiO 3 activator provides a new orientation for the preparation of MOF-derived carbons with rich pores, high surface area, and facilitates the large-scale application of MOF-derived carbons.