Microstructure and Mechanical Properties of Multicomponent Metal Ti(C,N)-Based Cermets

Ti(C,N)-based cermets with multicomponent ingredients were prepared using vacuum sintering technology. The effect of molding agents, binder phase and sintering temperature on Ti(C,N)-based cermets were studied. The optimum molding performance was obtained by adding 2% polyvinyl alcohol (PVA-1788). The microstructure and mechanical properties of Ti(C,N)-based cermets were investigated. The Ti(C,N)-based cermet with a weight percentage of TiC:TiN:Ni:Co:Mo:WC:Cr3C2:C = 40:10:20:10:7:8:4:1 and sintered at 1450 °C had the optimal mechanical properties. The relative bending strength, Vickers hardness, elastic modulus and wear resistance were 2010 MPa, 15.01 GPa, 483.57 GPa and 27 mg, respectively. Additionally, X-ray diffraction (XRD), backscatter scanning electron microscopy pictures (SEM–BSE), energy dispersive spectrometry (EDS) and optical micrographs of Ti(C,N)-based cermets were characterized.Keywords:Ti(C,N)-based cermet;vacuum sintering;NiCoMo powder;microstructure;mechanical properties