To improve the hot corrosion resistance, thickness controllable SiO 2 coating was electrodeposited on TiAl alloy. The hot corrosion behavior of the specimens contaminated with 75 wt.% Na 2 SO 4 + 25 wt.% NaCl salt mixture was investigated at 700 °C. Results showed that the generation of compact amorphous SiO 2 embedded with Na 2 Si 4 O 9 and cristobalite was responsible for the enhanced hot corrosion resistance. Moreover, the SiO 2 coating does not only act as a diffusion barrier to sulfur and chlorine but also decreases the oxygen partial pressure at the coating/alloy interface, therefore promoting the selective oxidation of Al to form protective Al 2 O 3 layer.