Li2CoTi3O8 and its composite nanofibers as high performance and long cycle lithium ion electrode materials

In this work, Li 2 CoTi 3 O 8 nanofibers and Li 2 CoTi 3 O 8 ·CoTiO 3 ·TiO 2 (LCT) composite nanofibers as anode materials in lithium-ion batteries (LIBs) were successfully prepared by a traditional electrospinning technology, and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), energy-dispersive spectrometer (EDS), X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA), and mappings. XRD confirms that the composite materials lattice planes well correspond to the patterns of Li 2 CoTi 3 O 8 , CoTiO 3 , and TiO 2 , respectively. SEM and TEM exhibits the fabricated composites are one-dimensional nanofibers with the diameter of 250~300 nm and 150~200 nm after annealing, respectively. The electrochemical properties of the materials for LIBs are investigated to indicate that the (LCT) composite nanofibers hold high reversible capacity of 201.68 mAh g −1 after 120 cycles and high rate capability at different current densities. Li 2 CoTi 3 O 8 ·CoTiO 3 ·TiO 2 (LCT) composite nanofibers were prepared through a electrospinning, which hold high reversible capacity of 201.68 mAh g −1 after 120 cycles and high rate capability at different current densities.