Microwave-assisted in situ polymerization of polycaprolactone/boron nitride composites with enhanced thermal conductivity and mechanical properties

Polycaprolactone/boron nitride (PCL/BN) composites were prepared by microwave-assisted ring-opening polymerization of ε-caprolactone (ε-CL). In order to improve the dispersibility and interfacial interaction between BN fillers and PCL matrix, hydroxyl functional BN (mBN) was first prepared to be used as a macroinitiator for ε-CL. Then BN grafted PCL (BN- g -PCL) copolymers were obtained via the in situ method, which acted as in situ compatibilizers in the PCL/BN composites. Various techniques were applied to characterize the mBN and PCL/BN composites. The Fourier transform infrared spectroscopy results confirm the structure of the BN- g -PCL copolymer. Field emission SEM graphs exhibit that, for the PCL/mBN composites, the mBN presents a homogeneous dispersion in the matrix and interfacial adhesion between the PCL and mBN is improved. These are beneficial for enhancing the thermal conductivity of the PCL/mBN composites. Notably, the PCL/mBN composite with 5 wt% mBN loading achieves the highest thermal conductivity of 0.55 W m −1 K −1 , which is 2.75 times higher than that of pure PCL, 0.20 W m −1 K −1 . This indicates that the excellent dispersion and interfacial adhesion could lead to the construction of continuous thermal conductive paths at a low BN loading and reduce the heat loss caused by phonon scattering in the interface. Furthermore, mBN could help to improve the mechanical properties of the composite. On adding 5 wt% mBN, the tensile strength and tensile modulus of the composite are 1.58 and 2.05 times higher, respectively, than those of PCL. © 2020 Society of Chemical Industry