Enhanced Catalytic Performance of Hierarchical MnOx/ZSM-5 Catalyst for the Low-Temperature NH3-SCR

A ZSM-5 zeolite with a hierarchical pore structure was synthesized by the desilication-recrystallization method using tetraethyl ammonium hydroxide (TEAOH) and cetyltrimethylammonium bromide (CTAB) as the desilication and structure-directing agents, respectively. The MnOx/ZSM-5 catalyst was synthesized by the ethanol dispersion method and applied for the low-temperature selective catalytic reduction of NOxwith NH3. The results showed that NOxconversion of the hierarchical MnOx/ZSM-5 catalyst could reach 100% at about 120 °C and could be maintained in the temperature range of 120–240 °C with N2selectivity over 90%. Furthermore, the hierarchical MnOx/ZSM-5catalyst presented better SO2resistance performance than the traditional catalyst in the presence of 100 ppm SO2at 120 °C. XRD, SEM, TEM, XPS, BET, NH3-TPD, and TG were applied to characterize the structural properties of the MnOx/ZSM-5 catalysts. These results showed that the MnOx/ZSM-5 catalyst had micropores (0.78 nm) and mesopores (3.2 nm) leading to a larger specific surface area, which improved the mass transfer of reactants and products while reducing the formation of sulfates. The better catalytic performance over hierarchical MnOx/ZSM-5 catalyst could be attributed to the higher concentration of Mn4+and chemisorbed oxygen species and higher surface acidity. The improved SO2resistance was related to the catalyst’s hierarchical pore structure.Keywords:hierarchical pore structure;MnOx/ZSM-5;NH3-SCR;SO2resistance