Pt Nanowire-Anchored Dodecahedral Ag3PO4{110} Constructed for Significant Enhancement of Photocatalytic Activity and Anti-Photocorrosion Properties: Spatial Separation of Charge Carriers and PhotogeneratedElectron Utilization

Pt nanowire-anchored dodecahedral Ag3PO4{110} was constructed for organics photodegradation. SEM and TEM images confirmed that the Pt nanowires were grafted on dodecahedral Ag3PO4, which was entirely bounded by {110} facets. All the X-ray diffraction peaks of the samples were indexed to the body-centered cubic phase of Ag3PO4, indicating that Pt nanowire-anchored dodecahedral Ag3PO4well maintained the original crystal structure. The rhombic dodecahedral Ag3PO4entirely bounded by {110} facets achieved high photocatalytic activity. Due to the formation of a Schottky barrier, the Pt nanowires improved the separation of the charge carriers of Ag3PO4. Furthermore, they provided a fast expressway to transfer the photogenerated electrons and prolonged the lifetime of the charge carriers via long-distance transport, resulting in the accumulation of holes on Ag3PO4for organics degradation. More importantly, the Pt nanowires improved the reduction potential of the photogenerated electrons for O2reduction to ·O2−, which enhanced the photocatalytic activity and anti-photocorrosion properties of Ag3PO4. We found that 99.5% of Rhodamine B (RhB) could be removed over 0.5ωt% Pt nanowire-anchored dodecahedral Ag3PO4within 10 min. Even after 10 cycles, the photocatalytic activity was still high. photoluminescence (PL), time-resolved photoluminescence (TRPL), UV–vis diffuse reflectance spectra (UV–visDRS), and photoelectrochemical analysis showed that Pt nanowire-anchored dodecahedral Ag3PO4exhibited lower bandgap, higher photocurrent intensity, better electronic conductivity, and longer charge carriers lifetime than other types of Ag3PO4crystals. Radical trapping experiments and electron paramagnetic resonance (EPR) analysis demonstrated that the holes were the main active species for organics photodegradation.Keywords:Pt nanowire-anchored dodecahedral Ag3PO4{110};anti-photocorrosion;spatial charge carriers’ separation;photogenerated electron utilization;oxygen reduction