Highly selective uranium adsorption on 2-phosphonobutane-1,2,4-tricarboxylic acid-decorated chitosan-coated magnetic silica nanoparticles

The separation and recovery of uranium resources from nuclear waste solutions is important for achieving uranium reuse and environmental protection. In this study, a novel adsorbent, 2-phosphonobutane-1,2,4-tricarboxylic acid (PBTCA)-decorated chitosan-coated magnetic silica nanoparticles, was fabricated and applied to the highly selective adsorption of uranium from aqueous solution. Selective sorption in a multi-ion solution (pH 4.0) containing 14 coexisting cations resulted in CoFe 2 O 4 @SiO 2 @CS-PBTCA showing an excellent uranium adsorption capacity of up to 83.16 mg g −1 , which was much higher than that of ungrafted CoFe 2 O 4 @SiO 2 @CS (29.99 mg g −1 ). The adsorbent also exhibited higher acid resistance than uncoated silica adsorbent under pH 1.0 conditions, with CoFe 2 O 4 @SiO 2 @CS-PBTCA showing barely any iron and cobalt leaching, while CoFe 2 O 4 @CS-PBTCA showed iron and cobalt leaching amounts of 2.97 and 0.93 mg L −1 , respectively. The desorption experiment used 0.2 M PBTCA (pH 1.0) as eluent, with the results showing that uranium ions were readily and rapidly desorbed. Furthermore, CoFe 2 O 4 @SiO 2 @CS-PBTCA maintained outstanding stability and adsorption performance after five reuse cycles. The mechanism for U(VI) removal was investigated by X-ray photoelectron spectroscopy and Fourier transform infrared spectroscopy, with the results suggesting that the adsorbent binds to uranium mainly though oxygen atoms of carboxyl groups and phosphonic groups in PBTCA. This strategy shows strong potential for developing a variety of novel, highly active, acid resistance, and reusable immobilized functional magnetic materials for effective separation of uranium from a multi-ion solution.