Electrospun Fe2MoC/C nanofibers as an efficient electrode material for high-performance supercapacitors

Bimetallic carbides have aroused wide attention for energy-storage applications recently. In this work, one-dimensional Fe 2 MoC/CNFs (Fe 2 MoC/C nanofibers) are successfully synthesized via a facile electrospinning method for the first time. To obtain the most integrated structure between the Fe 2 MoC nanoparticles and carbon nanofibers , we explore the optimal heating rate during the carbonization treatment. Fe 2 MoC/CNFs exhibits an integrated one-dimensional structure under 800 °C with a heating rate of 5 °C/min. As revealed in the experimental results, Fe 2 MoC/CNFs possesses a high specific surface area of 196.9 m 2 /g, a high specific capacitance of 347.8 F/g at the current density of 1 A/g, an excellent rate capability of 91% capacitance retention from 1 A/g to 40 A/g, and shows superior cycling stability with the capacitance retention of about 85.6% and Coulombic efficiency of about 100% after 5000 cycles. An asymmetric supercapacitor coin-cell device using Fe 2 MoC/CNFs as the positive electrode displays an energy density of 14.5 Wh/kg at a power density of 300 W/kg and an outstanding cycling life of 93% retention after 5000 cycles. The impressive electrochemical performance indicates that the Fe 2 MoC/CNFs composite is a promising material for efficient supercapacitors .