Influence of B4C coating on graphitization for diamond/WC-Fe-Ni composite

Diamond/WC-Fe-Ni composite is a potential composition for impregnated diamond drill bits. It is necessary to avoid the graphitization of the diamond from Fe and Ni under the powder metallurgy process. Boron carbide (B 4 C) was coated on diamond, and diamond/WC-Fe-Ni composites were consolidated by hot pressing at different temperatures. The influences of sintering temperature and interfacial structure on bending strength and wear behavior were investigated. The bending strength for diamond/WC-Fe-Ni composite was dependent on matrix densification and interfacial graphitization. Un-coated diamond was eroded by Fe-Ni matrix and partially converted to graphite during the sintering process at all sintering temperatures. In opposite, B 4 C coating was beneficial to matrix densification at a lower sintering temperature, and delayed the appearance of graphitization to around 1300 °C. Therefore, the diamond/WC-Fe-Ni composites with B 4 C coating exhibited larger bending strength and better wear behavior at a relative low sintering temperature.