Facile, economical and environment-friendly synthesis process of porous N-doped carbon/SiOx composite from rice husks as high-property anode for Li-ion batteries

To enhance electrochemical properties of C/SiO x composite for business application, N-doped carbon/SiO x composite has been successfully fabricated using rice husks as the raw material of both C and Si sources and urea as N source via an environmentally friendly and economically viable strategy. The obtained N@C/SiO x composite exhibits a porous irregular particle morphology with a high specific surface area. SiO x particles are uniformly dispersed in N-doped C skeleton. As an anode material for Li-ion batteries, the porous structure, N doping and high reduction degree of SiO 2 endow N@C/SiO x electrodes with an outstanding reversible capacity up to 1018.5 mAh/g at 0.1 A/g and a remarkable initial coulombic efficiency of 72.2%, which is larger than that of carbonized rice husks (45.7%). Even if the current density rises to 1.0 A/g, the reversible specific capacity can maintain at 623.3 mAh/g with a capacity degradation of merely 4.0% after 1000 cycles.