Functional packaging films originating from hemicelluloses laurate by direct transesterification in ionic liquid

An alternative transesterification with vinyl laurate (VL) was applied for chemical modification of hemicelluloses (HC) to prepare functional packaging films. Successful transesterification was confirmed by FT-IR and NMR. Semitransparent laurated HC (LHs) films were prepared by solvent casting method. SEM indicated the ordered honeycomb-patterned surface and the dense cross section of LHs films. The LHs films exhibited excellent hydrophobicity with water contact angle about 120° and the enhanced mechanical properties with tensile strength and elongation at break as 33.94 ± 3.09 MPa and 22.41 ± 2.87%, respectively. The water vapor permeability (WVP) and oxygen permeability (OP) values of LHs films ranged from 1.59 ± 0.07 to 2.23 ± 0.11 (10 −10 ·g/m·s·Pa) and 1.21 ± 0.04 to 4.24 ± 0.30 (cm 3 · μ m/m 2 ·d·kPa), respectively. Moreover, the films had acceptable antioxidant activity. In terms of these properties, the shelf life of green chilies could be largely extended to 15 days after packing with LHs films.