Sol-gel processing of Eu3+ doped Li6CaLa2Nb2O12 garnet for efficient and thermally stable red luminescence under near-ultraviolet/blue light excitation

Li 6 CaLa 2 Nb 2 O 12 garnet is known as an electrolyte for Li + -batteries. The sol–gel processing of this work yielded a series of phase pure Li 6 CaLa 2(1− x ) Nb 2 O 12 : x Eu 3+ garnet phosphors (LCLNG: x Eu; x  = 0–0.40) that are efficiently excitable with either near-ultraviolet (NUV, ~350–400 nm) or blue (~450–475 nm) light to produce dominantly strong 610 nm red emission. Increasing Eu 3+ substitution for La 3+ (larger x ) led to smaller cell constant and lower symmetry of the (La/Ca)O 8 dodecahedron, as revealed via Rietveld structure refinement, and meanwhile narrower bandgap. The excitation/emission behaviors and high quenching concentration of Eu 3+ ( x  = 0.35) were interpreted for the phosphor series by considering bandgap energy, (La/Ca)O 8 distortion and local arrangement of atoms. The LCLNG:0.35Eu optimal phosphor was analyzed to have absolute quantum yields of ~51% (λ ex  = 393 nm) and 65% (λ ex  = 463 nm), fluorescence lifetime of ~0.70 ms and color coordinates of around (0.65, 0.35) at room temperature and to be able to retain as high as ~85% of its room-temperature intensity at 423 K for the 610 nm emission. Application of LCLNG:0.35Eu further indicated that this phosphor has the potential to be used in NUV-excited LEDs.