High temperature anti-oxidative and tunable wave absorbing SiC/Fe3Si/CNTs composite ceramic derived from a novel polysilyacetylene

With the rapid development of high power electromagnetic (EM) equipment and high-speed aircraft, the powerful and high oxidation-resistance absorbers are fundamentally desirable for the EM field. Herein, a novel high temperature anti-oxidative SiC/Fe 3 Si/CNTs composite is synthesized by a facile polymer derived ceramic (PDC) route from a Fe-containing polysilyacetylene (PSA). The microstructure of as-prepared SiC/Fe 3 Si/CNTs composite absorber is featured by micro-sized SiC ceramic grains with spherical Fe 3 Si nanoparticles and carbon nanotubes (CNTs) attached to. The vector network analyzer tests show a tunable wave-absorbing performance by adjusting the thickness of layer, and the effective bandwidth (the reflection loss < −10 dB) is 3.3–16.8 GHz for the sample S-1400 (heat treatment at 1400 °C in nitrogen flow). The minimal RL value is −41.2 dB at 10.5 GHz at a thickness of 2 mm and an effective bandwidth is nearly 4 GHz (12.9–16.9 GHz) at the thickness of only 1.5 mm. Moreover, after the oxidation treatment at 800 °C in the air, this absorber maintains the main structure and shows a good high temperature oxidation resistance . This absorber still remains excellent wave absorption property, in view of a minimal RL value of −40 dB at the thickness of 3 mm and a bandwidth of 4.8 GHz (10.4–15.2 GHz) at the thickness of 2.5 mm. The mechanism of high EM wave absorption performance is studied and attributed to the impendence matching, polarization, and the magnetic properties . Thus, the SiC/Fe 3 Si/CNTs composite is a promising EM absorber for high-temperature EM wave-absorbing applications.