Photoluminescence Characteristics of Sn2+ and Ce3+-Doped Cs2SnCl6 Double-Perovskite Crystals

In recent years, all-inorganic lead-halide perovskites have received extensive attention due to their many advantages, but their poor stability and high toxicity are two major problems. In this paper, a low toxicity and stable Cs2SnCl6double perovskite crystals were prepared by aqueous phase precipitation method using SnCl2as precursor. By the XRD, ICP-AES, XPS, photoluminescence and absorption spectra, the fluorescence decay curve, the structure and photoluminescence characteristics of Ce3+-doped and undoped samples have been investigated in detail. The results show that the photoluminescence originates from defects. [SnSn4+2++VCl] defect complex in the crystal is formed by Sn2+substituting Sn4+. The number of defects formed by Sn2+in the crystal decreases with Ce3+content increases. Within a certain number of defects, the crystal luminescence is enhanced with the number of [SnSn4+2++VCl] decreased. When Ce3+is incorporated into the crystals, the defects of [Ce3+Sn4++VCl] and [SnSn4+2++VCl] were formed and the crystal show the strongest emission. This provides a route to enhance the photoluminescence of Cs2SnCl6double perovskite crystals.Keywords:lead-free perovskite;Cs2SnCl6;doping;photoluminescence