Highly Efficient Dynamic Degradation of Methylene Blue on Hierarchical Nitrogen/Cobalt-Co-Doped Carbonaceous Beads with Diffusion Promoting Nanostructures

Graphical Hierarchical Co/N-co-doped carbonaceous beads with diffusion-promoting nanostructures were prepared for organic pollutant degradation. Fixed-bed column degradation experiments were carried out to evaluate the dynamic degradation and potential industrial applications with various simulated real conditions. Additionally, SA/N−Co x O y catalyst was prepared with waste cobalt solution, with the goal of recycling waste ion solutions. Un-restricted diffusion channels for ions and molecules within catalytic composites is of practical significance for environmental remediation with aqueous reaction systems. Herein, hierarchical Co/N-co-doped carbonaceous beads with diffusion-promoting nanostructures for activating peroxymonosulfate (PMS) were prepared through a seaweed-based hydrogel strategy. Several technologies were applied to characterize resultant samples including XRD, SEM, TEM, XPS and N 2 adsorption-desorption. The degradation was carefully tested in simulations of real conditions such as in running water, laboratory waste liquid, and seawater, which indicated that the catalyst/PMS system has a practical and a wide range of degradation capacity. Moreover, SA/N−Co x O y could also prepared with waste cobalt solution, and also showed relatively good catalytic performance. In contrast to other works which mostly concentrated on the study of static testing, this research is mainly concerned with dynamic degradation. Batch and fixed-bed column degradation experiments were simultaneously carried out to evaluate the efficiency and potential industrial applications, which revealed that the as-prepared sample led to the fast removal of 90.26% of MB within 400 minutes and continuously degraded the dye for 25 h at 298 K. The recycling performance was also investigated by means of dynamic degradation tests, which only showed a slight decline with time.