Synthesis of monolithic SiC aerogels with high mechanical strength and low thermal conductivity

The monolithic silicon carbide (SiC) aerogels were converted from catechol-formaldehyde/silicon composite (CF/SiO 2 ) aerogels through carbothermal reduction and calcination . In the process of preparing the CF/SiO 2 aerogel, a new method was proposed to produce more silicon carbide and enhanced the mechanical properties of the SiC aerogel. This method was realized by adding an alkaline silica sol as supplemental silicon source. The principle process of CF/SiO 2 aerogels converting to SiC aerogels was discussed based on experiment and results analysis, while the microstructure, mechanical properties, and thermal properties of the prepared SiC aerogels were investigated. The results show that the as-synthesized SiC aerogels consist of β-SiC and a small amount of α-SiC nanocrystalline . It possessed a mesoporous structure and a low thermal conductivity 0.049 W/(m∙K), a relatively high compressive strength 1.32 MPa, and a relatively high specific surface area 162 m 2 /g. Due to their outstanding thermal and mechanical properties, the prepared SiC aerogels present potential applications in thermal insulation field, such as space shuttles and aerospace carrier thermal protection materials.