Ni-Al layered double hydroxide with regulated interlayer spacing as electrode for aqueous asymmetric supercapacitor

Using sodium oleate as surfactant and intercalating agent, a regulated Ni-Al layered double hydroxide (NA-LDH-OA) nanosheets with a high interlayer space were prepared by two-phase method combined with a short reflux process and mild solvothermal reaction. In the process of electrochemical reaction, the electron transport is accelerated by the higher base spacing of the NA-LDH-OA ultrathin nanosheets. The as-prepared material exhibited a high specific capacity (1.040 C cm −2 at a current density of 1.68 mA cm −2 ) and good cycling performance (capacity retention of 88.25% after 2000 cycles) in a three-electrode system. Moreover, an aqueous asymmetric supercapacitor (ASC) was assembled using the synthesized NA-LDH-OA nanosheets as the positive electrode and activated carbon (AC) as the negative electrode. The aqueous ASC device (NA-LDH-OA-2//AC) achieved a high energy density of 40.26 Wh kg −1 at a power density of 943 W kg −1 , and a good cycling performance of 94.5% retention after 5000 cycles. These results demonstrated that the NA-LDH-OA nanosheets possess the potential for upcoming energy storage devices.