Polyarylene Ether Nitrile and Barium Titanate Nanocomposite Plasticized by Carboxylated Zinc Phthalocyanine Buffer

Barium titanate (BT) and polyarylene ether nitrile (PEN) nanocomposites with enhanced dielectric properties were obtained by using carboxylatedzinc phthalocyanine (ZnPc-COOH) buffer as the plasticizer. Carboxylated zinc phthalocyanine, prepared through hydrolyzing ZnPc in NaOH solution, reacted with the hydroxyl groups on the peripheral of hydrogen peroxide treated BT (BT-OH) yielding core-shell structured BT@ZnPc. Thermogravimetric analysis (TGA), transmission electron microscopy (TEM), TEM energy dispersive spectrometer mapping, scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and Fourier transform infrared (FTIR) demonstrated successful preparation of BT@ZnPc. The fabricated BT@ZnPc was incorporated into the PEN matrix through the solution casting method. Rheological measurements demonstrated that the ZnPc-COOH buffer can improve the compatibility between BT and PEN effectively. With the existence of the ZnPc-COOH buffer, the prepared BT@ZnPc/PEN nanocomposites exhibit a high dielectric constant of 5.94 and low dielectric loss (0.016 at 1000 Hz). BT@ZnPc/PEN dielectric composite films can be easily prepared, presenting great application prospects in the field of organic film capacitors.Keywords:barium titanate;polyarylene ether nitrile;zinc phthalocyanine;dielectrics;rheology