Synergistic effects and kinetics of rGO-modified TiO2 nanocomposite on adsorption and photocatalytic degradation of humic acid

Graphene oxide was prepared using the modified Hummers method and reduced graphene oxide (rGO) - titanium dioxide (TiO 2 ) nanocomposite was synthesised using the one-step hydrothermal treatment . The synergistic effects on adsorption and photocatalytic properties of the rGO-TiO 2 nanocomposite for the humic acid removal were systematically investigated. The results of X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and Raman and infrared (IR) spectroscopy indicate that GO was partially reduced to reduced graphene oxide (rGO) in the hydrothermal synthesis process and anatase TiO 2 nanoparticles uniformly grew on the surface of rGO. The photoelectron and photohole generated under visible light irradiation were effectively separated on the surface of rGO-TiO 2 . The rGO-TiO 2 nanocomposite exhibited higher photocatalytic activity as a result of the synergistic effects of surface functional groups for adsorption and the excellent conductivity for photocatalytic reaction. The effect of rGO-TiO 2 nanocomposite dosage, light intensity and system temperature on the removal of humic acid solution was investigated. The results show that the removal efficiency of humic acid increased with system temperature and light intensity. When the dosage of rGO-TiO 2 nanocomposite was 1.2 g/L, the temperature, the light intensity and the pH of this system was 303 K, 4.37 Wm −2 and 7, respectively, the removal efficiency of humic acid reached 88.7% under visible light irradiation.