Structural Controlling of Highly-Oriented Polycrystal 3C-SiC Bulks via Halide CVD

Highly-oriented polycrystal 3C-SiC bulks were ultra-fast fabricated via halide chemical vapor deposition (CVD) using tetrachlorosilane (SiCl4) and methane (CH4) as precursors. The effects of deposition temperature (Tdep) and total pressure (Ptot) on the orientation and surficial morphology were investigated. The results showed that the growth orientation of 3C-SiC columnar grains was strongly influenced byTdep. With increasingTdep, the columnar grains transformed from <111>- to <110>-oriented. The arrangement of <111>-oriented columnar grains was controlled byPtot. Lotus-, turtle-, thorn-, and strawberry-like surface morphologies were naturally contributed by different arrangements of <111>-oriented grains, and the deposition mechanism was discussed. The wetting behaviors of CVD-SiC samples by molten aluminum were also examined at 1173 K in a high vacuum atmosphere.Keywords:3C-SiC;chemical vapor deposition (CVD);orientation;surficial morphology;wettability