Photopolymerization synthesis of polyacrylic acid dispersant with methoxysilicon end groups and its application in a nano-SiO2 aqueous system

In order to improve the dispersity and stability of the nano-SiO 2 aqueous system with high solid content, a kind of polyacrylic acid dispersant with methoxysilicon end groups (KH590-PAA) was synthesized by photopolymerization of acrylic acid (AA) initiated with (3-mercaptopropyl)trimethoxysilane (KH590). After adding KH590-PAA into the nano-SiO 2 aqueous dispersion system (20 wt% solid content), the viscosity and the curing time of the system were measured with a rotational viscometer and the inverted bottle method. Moreover, the dispersion mechanism of KH590-PAA for the nano-SiO 2 aqueous system was researched by measuring the adsorption capacity, the particle size and the zeta potential of the nanoparticles with a conductivity meter, dynamic light scattering, SEM and TEM, respectively. The results showed that the methoxysilicon groups in KH590-PAA could react with hydroxyl groups on the surface of nano-SiO 2 in the process of stirring, which enhanced the adsorption capacity of the dispersant and then increased the surface charge of the particles. Therefore, electrostatic repulsion and steric hindrance effects between the SiO 2 nanoparticles could be further enhanced by adding the KH590-PAA dispersant, and then the nano-SiO 2 aqueous system exhibited better dispersity and stability. Besides, the dispersion properties of SiO 2 nanoparticles in water were closely related to the addition amount and the molecular weight of the KH590-PAA dispersant. © 2018 Society of Chemical Industry