One-pot facile route to fabricate the precursor of sulfonated graphene/N-doped mesoporous carbons composites for supercapacitors

A facile one-pot aqueous route is firstly proposed to fabricate the precursor of sulfonated graphene/N-doped mesoporous carbons composite (SG/NMC). SG/NMC for supercapacitor applications is subsequently obtained by thermal pyrolysis of this precursor. The obtained SG/NMC possesses the ordered mesostructures with both lattice unit parameter about 14.3 nm and much wider distributions of pore sizes, as well as delivers a specific surface area high up to 1039.65 m 2  g −1 . Likewise, SG/NMC exhibits a high specific capacitance about 304.2 F g −1 at 1.0 A g −1 , which is much higher than ordered mesoporous carbons (OMC, 128.9 F g −1 ) and N-doped mesoporous carbons (NMC, 223.3 F g −1 ). Moreover, the resultant carbon displays a capacitance of 209.2 F g −1 at a current density even up to 50 A g −1 and the capacity can be retained above 93% after 5000 cycles at 10 A g −1 . The strategy demonstrated here is therefore expected to open up new routes to fabricate graphene and mesoporous carbons composites in aqueous solutions for supercapacitor applications.