Improving the interfacial properties of carbon fiber–epoxy resin composites with a graphene-modified sizing agent

We successfully prepared a graphene-modified carbon fiber (CF) sizing agent with good dispersity and stability by dispersing reduced graphene oxide (RGO) into an emulsion-type sizing agent. RGO was obtained by the reduction of graphene oxide (GO) with the help of gallic acid. The influence of the graphene-modified sizing agent on the interfacial properties of the CF–epoxy resin composites was investigated with microbond testing and the three-point bending method. The results show that optimized interfacial properties were achieved when the size of the modified graphene was less than 1 μm, the content of RGO was 20 ppm, and the pH value of the sizing agent was 10.5. The interfacial shear strength of the composites reached 92.3 MPa, which was 29.6% higher than that of the composites with unmodified CFs. Compared with commercial-CF-fabric-reinforced composites, the interlaminar shear strength of the composites treated with the RGO-modified sizing agent increased by 21.5%. Both the interfacial and interlaminar failure morphologies of the composites were examined with scanning electron microscopy (SEM). The results show that a large amount of residual resin adhered to the surfaces of the CFs treated with the RGO-modified sizing agent; this indicated good interfacial properties between the CFs and the resin matrix. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136 , 47122.