Low-temperature activity and mechanism of WO3-modified CeO2-TiO2 catalyst under NH3-NO/NO2 SCR conditions

The CeO 2 -TiO 2 (CeTi) and CeO 2 /WO 3 -TiO 2 (CeWTi) catalysts were prepared by a sol-gel precipitation method and their NH 3 -NO/NO 2 selective catalytic reduction (SCR) performance was studied. N 2 O formation and effect of oxygen concentration on SCR performance over CeWTi catalyst were also investigated while varying the NO 2 /NO x ratio. Results indicate that fast SCR behavior of CeWTi catalyst has the best NH 3 -NO/NO 2 SCR performance due to the catalyst reoxidation rate by NO 2 higher than by O 2 . Compared with CeTi catalyst, CeWTi catalyst exhibits higher de-NO x performance under NH 3 -NO/NO 2 SCR conditions. As the CeTi and CeWTi catalysts exhibit similar redox property, addition of WO 3 provides more acid sites which accelerate the reaction between NH 4 NO 3 and NO to get a superior low-temperature activity. Amount of N 2 O formation shows a peak at 250 °C mainly derived from NH 4 NO 3 decomposition.