Adsorption of estrone with few-layered boron nitride nanosheets: Kinetics, thermodynamics and mechanism

Boron nitride Nanosheets (BNNSs) was fabricated with a method of heating the mixture of boric acid and urea in N 2 atmosphere and used to remove estrone (E 1 ) from water. The obtained BNNSs exhibited a higher surface area of 896 m 2 /g, a large pore volume of 0.76 cm 3 /g, and only few layers (0.398 nm) with the boric acid and urea ratio of 1:80. The layer number of BNNSs decreased from 15 to 4 with the mole ratio of boric acid and urea decreasing from 1:20 to 1:80, which was identified by SEM , TEM , AFM and BET measurements. More importantly, BNNSs presented an outstanding adsorption performance for estrone with the adsorption capacity of 249.15 mg E 1 /g BNNSs. The adsorption process could be best fitted by pseudo second-order kinetic model and the equilibrium data at different temperatures were well fitted by Langmuir isotherm model. The thermodynamics analysis revealed that E 1 adsorption on BNNSs was spontaneous (ΔG = −29.33 kJ mol −1 ), enthalpy-retarded (ΔH = 29.75 kJ mol −1 ), entropy-driven (ΔS = 198.26 J mol −1 K −1 ), and mostly chemical adsorption. The adsorption rates of E 1 in water were sharply enhanced with thinner BNNSs as absorbents and removal efficiency by BN-60 regenerated after 6 times was above 95%, it was shown that the surface areas, mesopores and remarkable structure played important roles in the adsorption process. The firmness of E 1 onto BNNSs and the stability of adsorption efficiency made BNNSs as a potential absorbent for efficient removal of E 1 from wastewater.