Effect of co-solvent on the structure and dielectric properties of porous polyimide membranes

A series of porous polyimide (PI) membranes with 3,3',4,4'-benzophenonetetracarboxylic dianhydride (BTDA) and 4,4'-diaminodiphenyl ether (ODA) in the different ratio of co-solvent (N, N-dimethylacetamide (DMAC)/1, 4-butyrolactone (GBL)) were prepared by a novel wet phase inversion method. The influence of co-solvent on the structure and dielectric properties of membranes were investigated. PI membranes changed from finger-like structure to spongy-like structure with the increasing of the GBL content since the intermolecular interaction between PI induced by GBL. The proportion and size of finger-like structure gradually decreased with the increase of GBL content in DMAC/GBL co-solvent. Although PI membranes exhibited low dielectric permittivity ranges from 1.7–2.5, the dielectric breakdown strengths were also relatively low. In particular, the PI from pure GBL yielded the highest breakdown strength (260.05 kV mm−1) since the low proportion of macrovoids and defects. Moreover, when the ratio of GBL/DAMC was 84/16, the resultant PI membrane possessed a low dielectric constant (1.99) as well as relatively high breakdown strength (100.53 kV mm−1). Therefore, porous PI membraness may be potential in many applications of electronics and microelectronics.