Thermal Emittance of $$\hbox {La}_{0.7}\hbox {Ca}_{0.3-x}\hbox {K}_x\hbox {MnO}_3$$ Coatings on Aluminum Substrate

A novel thermal control coating was presented based on the thermochromism of manganite. The pigment of K-doped manganite nanoparticles was dispersed into polymer matrix to prepare the coating with curing below 200  \(^{\circ }\) C. The nanoparticles size mainly distributes around 100–200 nm, and it shows a comparable stoichiometric ratio. The phase transition of the nanoparticles was observed from ferromagnetic metallic to paramagnetic insulator state. With increasing K doping level, the phase transition temperature increases, achieving controllable adjustment. Coating surface with and without pore defect was obtained by different polymer matrix. A sharp emittance variation was observed with increasing temperature in K-doped coating. The variation magnitude of emittance is up to 0.46, which is attractive to space thermal control. It is suggested that the pigment content of 50 wt% is sufficient to realize a large emittance variation.