Cobalt encapsulated N-doped defect-rich carbon nanotube as pH universal hydrogen evolution electrocatalyst

Exploring efficient and economical Pt-free electrocatalysts is of great significance for the electrocatalytic hydrogen evolution reaction (HER). However, the rational design on an industrial scale is a formidable challenge. Herein, we reported a facile calcination at controlled temperatures to fabricate rationally assembled cobalt nanoparticles embedded in defect-rich N-doped carbon nanotubes (Co-NCNTs), which was derived from low-cost dicyanadiamide thermally polymerized with cobalt precursor forming metal-organic frameworks, then further calculation leading to final products. The as-obtained samples were endowed with high content of N as electrocatalytic active site, defect-rich structure and excellent synergistic effect between cobalt nanoparticles and carbon nanotubes toward electrocatalytic HER . As expected, Co-NCNTs were highly active and long-term stable with onset potentials of c.a. 15 mV in acidic electrolytes (0.5 M H 2 SO 4 ), 70 mV in alkaline (1 M KOH) and 300 mV in neutral media (pH 7). Specially, to achieve the current density of 10 mA cm −2 , the overpotential of 103 mV in acid, 204 mV in alkaline and 337 mV in neutral media was obtained. The enhanced HER performance was discussed in detail by adjusting the molar ratio of precursor and metal species. Moreover, the present synthetic route is easy to scale up and expand to other non-noble metal and alloy.