Fabrication of nano copper oxide evenly patched on cubic sodium tantalate for oriented photocatalytic reduction of carbon dioxide

A synthetic process was exploited to fabricate patchy CuO evenly planted on cubic NaTaO 3 for photocatalytically reducing CO 2 in isopropanol. The nano patches of CuO with about 15 nm in size were uniformly distributed on the surface of NaTaO 3 via a phase-transfer protocol and solvothermal synthesis. The crystal phase, morphology, composition, optical absorption and charge separation of as-prepared CuO-NaTaO 3 were characterized by XRD, SEM, TEM, EDX, XPS, UV–Vis and PL. The results of photocatalytic reduction of CO 2 confirmed that the CuO patched NaTaO 3 possessed better ability to separate charge carriers and selectively reduce CO 2 to methanol than CuO directly loaded NaTaO 3 using the traditional liquid phase reduction procedure after comparing the methanol yields. Furthermore, 5 wt% CuO patched NaTaO 3 led to the highest methanol yield of 1302.22 μmol g −1 h −1 . A redox mechanism was proposed and illustrated in a schematic diagram.