Gas-permeation performance of metal organic framework/polyimide mixed-matrix membranes and additional explanation from the particle size angle

With MOFs of Cu 3 (BTC) 2 and ZIF-8 as the dispersed phases and four polyimides with CO 2 permeabilities ranging from 1.36 to 564 barrer as the continuous phase, the influence of metal organic frameworks on the gas-separation properties of mixed-matrix membranes (MMMs) was investigated. The results show that the gas permeabilities of all of the prepared MMMs greatly increased and even largely exceeded the predicted value of the Bruggeman model; for example, with the same Cu 3 (BTC) 2 loading of 21.3 vol %, the O 2 permeability increase rate of our prepared Cu 3 (BTC) 2 /Matrimide 5218-20 MMMs was 2.26 times, whereas that predicted by the Bruggeman model was only 1.05 times. In addition, when the gas permeability of the polymeric phase was far lower than the dispersed phase of ZIF-8 or Cu 3 (BTC) 2 compared with ZIF-8, which had a particle size ( R ) around 150 nm, Cu 3 (BTC) 2 of 5–15 µm showed a little better enhancing effect on the gas-permeation performance of the MMMs. In addition to the properties of the dispersed and continuous phases, we speculated that the ratio between R of the dispersed phase to the membrane thickness ( L ) played an important role for MMMs; the larger R / L was, the greater the gas permeability of the MMMs was. This speculation was initially evidenced by the ZIF-8/ODPA/TMPDA-20 MMMs with different L s. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135 , 45728.