In situ fabrication of ZnO@N-doped nanoporous carbon core-shell heterostructures with high photocatalytic and adsorption capacity by a calcination of ZnO@MOF strategy

This report describes the controllable encapsulation of ZnO nanoparticles with N-doped nanoporous carbon (N-NpC) via a simple fabrication and calcination of ZnO@ZIF-8 (zeolitic imidazolate framework). In the fabrication of ZnO@ZIF-8, ZnO was used both as the support and Zn source for the formation of ZIF-8. After calcination under N 2 atmosphere, the ZnO@N-NpC core-shell heterostructures were formed and characterized by IR, UV–vis, XRD , XPS , scanning electron microscopy (SEM) and transmission electron microscopy (TEM). As expected, the well-defined ZnO@N-NpC core-shell nanospheres demonstrated distinct photocatalytic activity and adsorption capacity in response to the dye methylene blue (MB) in aqueous solution, and the degradation efficiency of MB is up to 99% under UV irradiation for 20   min after catalysts were reused for 5 cycles and stored for two months. Therefore, it is reasonable to believe that the ZnO@N-NpC core-shell heterostructures are new-type nanomaterials for photodegradation of the organic pollutants from wastewater.