Thin film composite membranes functionalized with montmorillonite and hydrotalcite nanosheets for CO2/N2 separation

Montmorillonite (MMT) and Mg-Al hydrotalcite (HT) nanosheets were prepared via vigorous agitation and ultrasonic, respectively. In order to increase the permeability of CO 2 , poly (PEA-MMT-TMC)/PS and poly (PEA-HT-TMC)/PS composite membranes were prepared via interfacial polymerization by adding the dimensional (2D) inorganic nanosheets (MMT and HT) into the aqueous phase of PEA. And in consequence, the poly (PEA-MMT-TMC)/PS composite membrane showed CO 2 permeability of 15.87 barrer and the CO 2 /N 2 selectivity of 37 at 1.0   bar when the MMT concentration was 0.068   wt%. The poly (PEA-HT-TMC)/PS composite membrane also showed CO 2 permeability of 15.3 barrer and the CO 2 /N 2 selectivity of 40 at 1.0   bar when the HT concentration was 0.25   wt%. Compared with the controlled membrane (CO 2 permeability: 6.9 barrer, CO 2 /N 2 selectivity: 103), the CO 2 permeability increased after incorporating the inorganic nanosheets into the membranes and maintained the pretty CO 2 /N 2 selectivity. The addition of exfoliated MMT and HT could facilitate the gas permeation to improve the gas separation performance of the composite membranes. Also, the combination of inorganic nanosheets with organic membrane has a great potential application in the gas separation.