Ultrasonic Spray-Coating of Large-Scale TiO2 Compact Layer for Efficient Flexible Perovskite Solar Cells

Flexible electronics have attracted great interest in applications for the wearable devices. Flexible solar cells can be integrated into the flexible electronics as the power source for the wearable devices. In this work, an ultrasonic spray-coating method was employed to deposit TiO2nanoparticles on polymer substrates for the fabrication of flexible perovskite solar cells (PSCs). Pre-synthesized TiO2nanoparticles were first dispersed in ethanol to prepare the precursor solutions with different concentrations (0.5 mg/mL, 1.0 mg/mL, 2.0 mg/mL) and then sprayed onto the conductive substrates to produce compact TiO2films with different thicknesses (from 30 nm to 150 nm). The effect of the different drying processes on the quality of the compact TiO2film was studied. In order to further improve the film quality, titanium diisopropoxidebis(acetylacetonate) (TAA) was added into the TiO2-ethanol solution at a mole ratio of 1.0 mol % with respect to the TiO2content. The final prepared PSC devices showed a power conversion efficiency (PCE) of 14.32% based on the indium doped tin oxide coated glass (ITO-glass) substrate and 10.87% on the indium doped tin oxide coated polyethylene naphthalate (ITO-PEN) flexible substrate.Keywords:ultrasonic spray;titanium oxide;flexible perovskite solar cells;low temperature;large area