Synthesis of selenium/EDTA-derived porous carbon composite as a Li–Se battery cathode

The carbon substrate with unique 3D macroporous structure has been prepared through the immediate carbonization of ethylenediaminetetraacetic acid (EDTA) and KOH mixture. The porous carbon composed of micro- and small mesoporous (2–5 nm) structure has a BET specific surface area of 1824.8 m 2  g −1 . The amorphous and nanosized Se is uniformly encapsulated into the porous structure of porous carbon using melting diffusion route, and the weight content of Se in target Se/C composite can be as high as ~50 %. As an Li–Se battery cathode, the Se/C composite delivers a reversible (2nd) discharge capacity of 597.4 mAh g −1 at 0.24C and retains a discharge capacity of 538.4 mAh g −1 at 0.24C after 100 cycles. Furthermore, the composite also has a stable capacity of 291.0 mAh g −1 at a high current of 4.8C. The high specific area and good porous size of EDTA-derived carbon substrate may a be responsibility for the excellent electrochemical performances of Se/C composite.