Selective methanation of CO over Ni/Al2O3 catalyst: Effects of preparation method and Ru addition

Four methods were adopted to prepare samples 20%NiO/Al 2 O 3 with calcination fixed at 500 °C, which were then reduced into 20%Ni/Al 2 O 3 and used as catalysts for reaction of selective methanation of CO in H 2 -rich gas (CO-SMET). XRD and TPR measurements indicate that nickel aluminates were formed in the calcined samples and their formation was influenced by preparation methods. Higher temperatures were required to reduce the calcined samples more efficiently and to achieve a higher catalytic activity for CO-SMET. Among the four methods, the precipitation method using ammonium carbonate as precipitant produced the highest catalytic activity both for CO methanation and for CO 2 methanation after reduction at 800 °C for 2 h. The calcined sample 20%NiO/Al 2 O 3 prepared with the method was therefore used as support and impregnated with Ru 3+ solution. Ru addition promoted reduction of Ni 2+ ions in the calcined sample even at the low temperatures of 400 °C and 500 °C. The catalyst 1%Ru–20%Ni/Al 2 O 3 reduced at 500 °C thus had a superior performance, removing CO to ca. 30 ppm with a selectivity as high as 75% at reaction temperature of 220 °C.