Efficiency enhancement of perovskite solar cells by fabricating as-prepared film before sequential spin-coating procedure

Sequential spin-coating procedure is a widely adopted strategy to prepare CH 3 NH 3 PbI 3 on mesostructured TiO 2 electrode for organolead halide perovskite-based solar cells. However, this method suffers from the rough surface and excessively residual PbI 2 in the resulting perovskite film, deteriorating the device performance seriously. Herein, a facial modified sequential solution deposition method, by introducing an as-prepared CH 3 NH 3 PbI 3 and PbI 2 film before the traditional two-step process, was proposed to fabricate the perovskite-based solar cell with smooth morphology and trace amount of remaining PbI 2 . The optimal as-prepared film introduced improves the efficiency of CH 3 NH 3 PbI 3 solar cells from 9.11% to 11.16%. The enhancement of device performance can be attributed to the increased light absorption ability and decreased recombination rate of carriers in CH 3 NH 3 PbI 3 absorber.