Palladium deposits spontaneously grown on nickel foam for electro-catalyzing methanol oxidation: Effect of precursors

Methanol, a high-energy substance, is widely used for green fuel cells. However, the sluggish electrochemical methanol oxidation reaction (MOR) on state-of-the-art catalysts still requires for exploring high-performance and low-cost materials to further promote the reaction kinetics at low overpotentials. Here we carried out the first electrocatalytic comparison study of two Ni foam-supported Pd nanomaterials (Pd-2-Ni and Pd-4-Ni, respectively), obtained through the spontaneous galvanic replacement of Ni with different palladic precursors ([PdCl 4 ] 2- and [PdCl 6 ] 2− , respectively), toward MOR. With replacement, Pd deposits with discrepant arrangements and coverages were grown on the porous Ni support. Compared to commercial Pd/C, both Pd-2-Ni and Pd-4-Ni exhibited better mass activity and catalytic durability for MOR in alkaline media . More interestingly, different palladic precursors made a significant effect on the catalytic performance of the Ni foam-supported Pd deposits. In Pd-4-Ni, the 2:1 stoichiometric replacement of Ni with [PdCl 6 ] 2− enabled the incompact arrangement of Pd structures, with more exposure of Ni atoms adjoined to Pd atoms on the catalytic interface compared to Pd-2-Ni. As a result, with the favorable Ni-neighbor-Pd regime and the higher utilization efficiency of Pd atoms, the synthesized Pd-4-Ni catalyst provided a mass activity of approximately 1.5 times higher than Pd-2-Ni toward MOR.