Surface modification and characterization of 8-hydroxyquinoline aluminum/nano-TiO2

8-hydroxyquinoline aluminum/nano-TiO 2 composites were prepared via in situ. In order to make a better combination of the two component, Octavinyl-T8-silsesquioxane (8-vinyl POSS) was introduced into the composite system . The structure and properties of the samples were characterized by XRD , SEM, XPS , UV–visible absorption, Fluorescence spectra and Time-resolved emission-decay. These results show both β-phase and γ-phase of Alq 3 exist in the composite products. Meanwhile, the addition of nano-TiO 2 and 8-vinyl POSS does not change the crystalline and structure of as-prepared Alq 3 . Interestingly, however, XPS spectra shows that two new kinds of interaction forces emerge after the addition of 8-vinyl POSS, owing to the formation of Al–O–Si and Si–O–Ti bond, presumably. Besides, the emission intensity of Alq 3 /nano-TiO 2 and Alq 3 /8-vinyl POSS/nano-TiO 2 increases by 22% and 33%, respectively. The addition of TiO 2 and 8-vinly POSS will not affect the position of emission peak, but will increase the transmission efficiency in electron–hole pairs. In the meantime, surprisingly, the modified Alq 3 has a longer lifetime than as-prepared Alq 3 .