Highly photocatalytic activity of brookite/rutile TiO2 nanocrystals with semi-embedded structure

A facile solvothermal approach was used to prepare brookite-type TiO 2 nanocrystals with different phase content and structure, accomplished by adjusting the ratio of TiCl 4 to t -BuOH. The obtained biphasic brookite/rutile TiO 2 nanocrystals showed a high brookite weight content (72%). The photocatalytic degradation of phenol under UV-irradiation was used to determine the synergetic effect from the combination of different phases ( e.g. , brookite, anatase, and rutile). The biphasic NST-4 composed of brookite and rutile exhibited the highest degradation rates, with rate constants three times higher than commercial Degussa P-25. Detailed analysis found that, besides phase composition and content, the semi-embedded structure was essential to obtain a superior activity of biphasic TiO 2 samples.