Photocatalytic degradation of methyl blue using Fe2O3/TiO2 composite ceramics

Using home-made Fe 2 O 3 /TiO 2 nanopowders as raw material, Fe 2 O 3 /TiO 2 composite ceramic was fabricated in order to use as photocatalysts in practical water purification treatment. The effects of sintering temperature on its phase variation, physical properties and photocatalytic properties were investigated. With sintering temperature increases, the anatase TiO 2 transforms into rutile phase, and reacts with hematite Fe 2 O 3 to form pseudobrookite Fe 2 TiO 5 . Above 800   °C, only Fe 2 TiO 5 and rutile TiO 2 were observed. Correspondingly, the porosity and the photocatalytic activity of Fe 2 O 3 /TiO 2 composite ceramic decreased, especially for samples sintered at 1000   °C, obvious decline in degradation efficiency was observed. The further investigation on photocatalytic degradation of methyl blue (MB) were carried out using ceramics sintered at 880   °C (TFC-880), which exhibited moderate physical and photocatalytical properties. The result showed that TFC-880 exhibited a high photodegradation capability for MB under either UV or visible light. Even in the third circle, it also showed a high degradation rate, meaning it has an extended application such as water treatment.